{"id":20493,"date":"2026-10-01T16:08:13","date_gmt":"2026-10-01T08:08:13","guid":{"rendered":"https:\/\/aobosteel.com\/?page_id=20493"},"modified":"2026-10-16T00:47:15","modified_gmt":"2026-10-15T16:47:15","slug":"l6-tool-steel-tensile-properties","status":"publish","type":"page","link":"https:\/\/aobosteel.com\/es\/l6-tool-steel-tensile-properties\/","title":{"rendered":"Propiedades de tracci\u00f3n del acero para herramientas L6 despu\u00e9s del revenido"},"content":{"rendered":"

Propiedades de tracci\u00f3n del acero para herramientas L6 despu\u00e9s del revenido<\/h1>\n\n\n\n

El L6 es el acero para herramientas de baja aleaci\u00f3n al que recurren los talleres cuando un troquel debe absorber impacto en lugar de resistir abrasi\u00f3n, y los valores que describen ese comportamiento son la resistencia a la tracci\u00f3n, el alargamiento y la reducci\u00f3n de \u00e1rea medidos en probetas revenidas. Las tablas siguientes re\u00fanen una colada de L6 sometida a cinco temperaturas de revenido y una comparaci\u00f3n del mismo grado L2 con y sin vanadio, ambas tomadas de la pr\u00e1ctica publicada. Cada cifra corresponde a la condici\u00f3n exacta de temple y revenido indicada junto a ella, por lo que cada fila debe leerse como el comportamiento medido en esa \u00fanica condici\u00f3n y no como un valor de dise\u00f1o. Este es un resumen de referencia de la pr\u00e1ctica publicada y no una especificaci\u00f3n nuestra.<\/p>\n\n\n\n

Qu\u00e9 miden las tablas<\/h2>\n\n\n\n

La primera tabla sigue un acero para herramientas L6 desde una condici\u00f3n dura y fr\u00e1gil despu\u00e9s de un revenido bajo hasta una condici\u00f3n m\u00e1s blanda y mucho m\u00e1s d\u00factil despu\u00e9s de un revenido alto. El acero se austeniz\u00f3 a 815 °C (1500 °F), se templ\u00f3 en aceite y se reven\u00f3 durante 2 h, y nada cambia en las cinco filas excepto la temperatura de revenido, por lo que las columnas muestran exactamente lo que un taller paga en dureza por cada punto de ductilidad que recupera. Las cifras provienen de Allegheny Ludlum Steel Corp.<\/p>\n\n\n\n

La segunda tabla responde a la pregunta cercana de qu\u00e9 hace el vanadio a esta familia de aceros. Se comparan dos coladas de L2 con el mismo nivel de carbono y casi el mismo cromo despu\u00e9s del mismo tratamiento, una con 0,20 por ciento de vanadio y otra sin \u00e9l, por lo que la diferencia entre las dos columnas se aproxima al efecto de esa \u00fanica adici\u00f3n.<\/p>\n\n\n\n

Propiedades de tracci\u00f3n del acero para herramientas L6 despu\u00e9s del revenido<\/h2>\n\n\n\n

Austenizado a 815 °C (1500 °F), templado en aceite y revenido 2 h<\/h3>\n\n\n\n
Temperatura de revenido, °C<\/th>Temperatura de revenido, °F<\/th>Resistencia a la tracci\u00f3n, MPa<\/th>Resistencia a la tracci\u00f3n, ksi<\/th>Alargamiento en 50 mm (2 in.), %<\/th>Reducci\u00f3n de \u00e1rea, %<\/th>Dureza, HRC<\/th><\/tr><\/thead>
205<\/td>400<\/td>2055<\/td>298<\/td>1.3<\/td>2.0<\/td>57<\/td><\/tr>
315<\/td>600<\/td>2004.72<\/td>290.75<\/td>4.3<\/td>9.3<\/td>53.5<\/td><\/tr>
425<\/td>800<\/td>1591.02<\/td>230.75<\/td>8.5<\/td>24.7<\/td>47<\/td><\/tr>
540<\/td>1000<\/td>1341.97<\/td>194.63<\/td>12.5<\/td>34.0<\/td>42<\/td><\/tr>
650<\/td>1200<\/td>966.2<\/td>140.13<\/td>18.8<\/td>47.2<\/td>32<\/td><\/tr><\/tbody><\/table><\/figure>\n\n\n\n

Fuente, Tool Steels (G. A. Roberts y G. Krauss), Tabla 8-10, Propiedades de tracci\u00f3n del acero para herramientas L6, p\u00e1gina impresa 158 del ejemplar consultado. Composici\u00f3n 0,68% C, 0,60% Mn, 0,65% Cr, 1,40% Ni, 0,20% Mo; temperatura de austenizaci\u00f3n 815 °C (1500 °F), templado en aceite, revenido 2 h. Cifras de Allegheny Ludlum Steel Corp. La fuente imprime las dos columnas de temperatura con sus encabezados intercambiados, y el emparejamiento usado aqu\u00ed sigue las temperaturas equivalentes en el eje de la Fig. 8-24 de la misma p\u00e1gina. Este es un resumen de referencia de la pr\u00e1ctica publicada y no una especificaci\u00f3n de Aobo Steel.<\/em><\/p>\n\n\n\n

La temperatura de revenido m\u00e1s baja de la tabla alivia la tensi\u00f3n de temple en lugar de ablandar el acero, y deja 57 HRC con 1,3 por ciento de alargamiento y 2,0 por ciento de reducci\u00f3n de \u00e1rea, lo que es una pieza con casi ninguna reserva antes de agrietarse. A partir de ah\u00ed la dureza cae en cuatro pasos m\u00e1s hasta 32 HRC a 650 °C mientras la reducci\u00f3n de \u00e1rea sube de 2,0 a 47,2 por ciento y el alargamiento de 1,3 a 18,8 por ciento. La resistencia sigue a la dureza hacia abajo, de 2055 MPa en el revenido m\u00e1s bajo a 966,2 MPa en el m\u00e1s alto.<\/p>\n\n\n\n

Dos de los pasos merecen se\u00f1alarse. Entre 205 y 315 °C el acero cede unos 50 MPa de resistencia a la tracci\u00f3n y 3,5 HRC mientras la reducci\u00f3n de \u00e1rea sube 7,3 puntos, por lo que la primera parte del rango de revenido compra ductilidad a bajo costo. El \u00faltimo paso, de 540 a 650 °C, cuesta 10 HRC y 376 MPa y devuelve 13,2 puntos de reducci\u00f3n de \u00e1rea, que es el punto en que el acero deja de comportarse como un filo de corte y empieza a comportarse como un material para troquel resistente al impacto. Las dos bandas de trabajo que la fuente nombra para el grado, 45 a 50 HRC para sierras para madera y 58 a 62 HRC para la mayor\u00eda de las dem\u00e1s aplicaciones, se sit\u00faan en los dos extremos de esta tabla, por lo que la tabla pone precio a la elecci\u00f3n entre un filo duro y un troquel que sobrevive al impacto.<\/p>\n\n\n\n

Acero para herramientas L2 con y sin vanadio<\/h2>\n\n\n\n
Propiedad<\/th>Acero A, L2 sin vanadio<\/th>Acero B, L2 con vanadio<\/th><\/tr><\/thead>
Resistencia a la tracci\u00f3n, MPa (ksi)<\/td>1523 (220.9)<\/td>1605 (232.8)<\/td><\/tr>
L\u00edmite de fluencia, MPa (ksi)<\/td>1384 (200.7)<\/td>1546 (224.2)<\/td><\/tr>
Relaci\u00f3n fluencia\/tracci\u00f3n<\/td>0.911<\/td>0.963<\/td><\/tr>
Alargamiento, %<\/td>9.6<\/td>10.4<\/td><\/tr>
Reducci\u00f3n de \u00e1rea, %<\/td>35.9<\/td>43.1<\/td><\/tr>
Dureza, HV<\/td>457<\/td>481<\/td><\/tr>
Impacto Izod, J (ft·lbf)<\/td>16.3 (12.0)<\/td>16.3 (12.0)<\/td><\/tr><\/tbody><\/table><\/figure>\n\n\n\n

Fuente, Tool Steels (G. A. Roberts y G. Krauss), Tabla 8-7, Propiedades mec\u00e1nicas de aceros L2 de medio carbono con y sin vanadio, p\u00e1gina impresa 148 del ejemplar consultado. Ambos aceros templados en aceite desde 840 °C (1545 °F) y revenidos a 425 °C (800 °F). Composici\u00f3n del acero A: 0,49% C, 0,76% Mn, 0,21% Si, 1,07% Cr. Composici\u00f3n del acero B: 0,50% C, 0,79% Mn, 0,31% Si, 0,98% Cr, 0,20% V. La cifra de impacto es un valor Izod en julios con la cifra en pies-libra entre par\u00e9ntesis. Este es un resumen de referencia de la pr\u00e1ctica publicada y no una especificaci\u00f3n de Aobo Steel.<\/em><\/p>\n\n\n\n

La adici\u00f3n de 0,20 por ciento de vanadio eleva la resistencia a la tracci\u00f3n en 82 MPa y el l\u00edmite de fluencia en 162 MPa con el mismo tratamiento, por lo que la relaci\u00f3n fluencia\/tracci\u00f3n pasa de 0,911 a 0,963, y mejora ligeramente la ductilidad en lugar de reducirla, con el alargamiento subiendo de 9,6 a 10,4 por ciento y la reducci\u00f3n de \u00e1rea de 35,9 a 43,1 por ciento. La dureza sube de 457 a 481 HV y el impacto Izod medido es el mismo 16,3 J (12,0 ft·lbf) para ambas coladas, por lo que la ganancia est\u00e1 en la resistencia y no en la tenacidad.<\/p>\n\n\n\n

Le\u00eddas juntas, las dos tablas muestran que la familia es coherente. El L6 y el L2 son ambos aceros de baja aleaci\u00f3n elegidos donde una herramienta debe sobrevivir al impacto, y en ambos casos la dureza, la resistencia y la ductilidad se mueven al comp\u00e1s de la temperatura de revenido. Mantenga la cifra de impacto en su propio contexto, porque pertenece a un ensayo sin entalla en una de las coladas de L2 y no es comparable con lecturas con entalla publicadas para otros grados.<\/p>\n\n\n\n

Datos de referencia relacionados<\/h2>\n\n\n\n

Los dos grados de estas tablas se describen con sus formas, rangos de secci\u00f3n y condiciones de entrega en acero para herramientas L6<\/a>, y la secuencia de temple, enfriamiento y revenido para el mismo grado se expone en Tratamiento t\u00e9rmico del acero para herramientas L6<\/a>. La elecci\u00f3n entre L6 y un grado para trabajo en caliente para un troquel de forja se desarrolla en Acero para herramientas H13 y 1.2714 (L6)<\/a>, la dureza que cada grado conserva despu\u00e9s de un revenido dado se representa en Tabla de revenido del acero para herramientas<\/a>, los valores de impacto para todo el rango se recopilan en tenacidad al impacto del acero para herramientas<\/a>, y el grupo al que pertenecen estos aceros se presenta en acero para herramientas endurecible al aceite<\/a>.<\/p>\n\n\n\n

\n

Propiedades de tracci\u00f3n del acero para herramientas L6, PDF imprimible<\/strong><\/p>\n\n

La resistencia a la tracci\u00f3n, el alargamiento, la reducci\u00f3n de \u00e1rea y la dureza del acero para herramientas L6 despu\u00e9s del revenido de 205 a 650 °C (400 a 1200 °F), con la comparaci\u00f3n de L2 con y sin vanadio, en un solo PDF con nuestros datos de contacto.<\/p>\n\n

\n
Descargar PDF<\/a><\/div>\n\n<\/div>\n<\/div>\n\n\n\n

Compilado de Tool Steels (G. A. Roberts y G. Krauss), Tabla 8-10 y Tabla 8-7, en las p\u00e1ginas impresas 158 y 148, el cap\u00edtulo sobre aceros para herramientas especiales de baja aleaci\u00f3n. La fuente imprime las columnas de temperatura de la Tabla 8-10 con sus encabezados intercambiados y los valores aqu\u00ed se emparejan seg\u00fan las temperaturas equivalentes impresas en la figura de la misma p\u00e1gina. Las tablas se reproducen tal como se publicaron y son un resumen de referencia y no una especificaci\u00f3n de Aobo Steel, por lo que deben tratarse como el comportamiento medido de una colada bajo un tratamiento t\u00e9rmico y no como un valor admisible de dise\u00f1o para un troquel particular.<\/p>","protected":false},"excerpt":{"rendered":"

L6 Tool Steel Tensile Properties After Tempering L6 is the low-alloy tool steel that shops reach for when a die has to absorb shock rather than resist abrasion, and the numbers that describe that behaviour are tensile strength, elongation and reduction of area measured on tempered specimens. The tables below collect one L6 heat carried […]<\/p>\n","protected":false},"author":1,"featured_media":0,"parent":0,"menu_order":0,"comment_status":"closed","ping_status":"closed","template":"","meta":{"_uag_custom_page_level_css":"","site-sidebar-layout":"default","site-content-layout":"","ast-site-content-layout":"normal-width-container","site-content-style":"default","site-sidebar-style":"default","ast-global-header-display":"","ast-banner-title-visibility":"","ast-main-header-display":"","ast-hfb-above-header-display":"","ast-hfb-below-header-display":"","ast-hfb-mobile-header-display":"","site-post-title":"disabled","ast-breadcrumbs-content":"","ast-featured-img":"","footer-sml-layout":"","ast-disable-related-posts":"","theme-transparent-header-meta":"","adv-header-id-meta":"","stick-header-meta":"","header-above-stick-meta":"","header-main-stick-meta":"","header-below-stick-meta":"","astra-migrate-meta-layouts":"default","ast-page-background-enabled":"default","ast-page-background-meta":{"desktop":{"background-color":"","background-image":"","background-repeat":"repeat","background-position":"center center","background-size":"auto","background-attachment":"scroll","background-type":"","background-media":"","overlay-type":"","overlay-color":"","overlay-opacity":"","overlay-gradient":""},"tablet":{"background-color":"","background-image":"","background-repeat":"repeat","background-position":"center center","background-size":"auto","background-attachment":"scroll","background-type":"","background-media":"","overlay-type":"","overlay-color":"","overlay-opacity":"","overlay-gradient":""},"mobile":{"background-color":"","background-image":"","background-repeat":"repeat","background-position":"center center","background-size":"auto","background-attachment":"scroll","background-type":"","background-media":"","overlay-type":"","overlay-color":"","overlay-opacity":"","overlay-gradient":""}},"ast-content-background-meta":{"desktop":{"background-color":"var(--ast-global-color-5)","background-image":"","background-repeat":"repeat","background-position":"center center","background-size":"auto","background-attachment":"scroll","background-type":"","background-media":"","overlay-type":"","overlay-color":"","overlay-opacity":"","overlay-gradient":""},"tablet":{"background-color":"var(--ast-global-color-5)","background-image":"","background-repeat":"repeat","background-position":"center center","background-size":"auto","background-attachment":"scroll","background-type":"","background-media":"","overlay-type":"","overlay-color":"","overlay-opacity":"","overlay-gradient":""},"mobile":{"background-color":"var(--ast-global-color-5)","background-image":"","background-repeat":"repeat","background-position":"center center","background-size":"auto","background-attachment":"scroll","background-type":"","background-media":"","overlay-type":"","overlay-color":"","overlay-opacity":"","overlay-gradient":""}},"footnotes":""},"class_list":["post-20493","page","type-page","status-publish","hentry"],"yoast_head":"\nL6 Tool Steel Tensile Properties After Tempering<\/title>\n<meta name=\"description\" content=\"Measured tensile strength, elongation, reduction of area and hardness for L6 tool steel after tempering from 205 to 650 C, with the L2 with and without vanadium comparison.\" \/>\n<meta name=\"robots\" content=\"index, follow, max-snippet:-1, max-image-preview:large, max-video-preview:-1\" \/>\n<link rel=\"canonical\" href=\"https:\/\/aobosteel.com\/es\/l6-tool-steel-tensile-properties\/\" \/>\n<meta property=\"og:locale\" content=\"es_ES\" \/>\n<meta property=\"og:type\" content=\"article\" \/>\n<meta property=\"og:title\" content=\"L6 Tool Steel Tensile Properties After Tempering\" \/>\n<meta property=\"og:description\" content=\"Measured tensile strength, elongation, reduction of area and hardness for L6 tool steel after tempering from 205 to 650 C, with the L2 with and without vanadium comparison.\" \/>\n<meta property=\"og:url\" content=\"https:\/\/aobosteel.com\/es\/l6-tool-steel-tensile-properties\/\" \/>\n<meta property=\"og:site_name\" content=\"AoboSteel\" \/>\n<meta property=\"article:publisher\" content=\"https:\/\/www.facebook.com\/profile.php?id=61565368220197\" \/>\n<meta property=\"article:modified_time\" content=\"2026-10-15T16:47:15+00:00\" \/>\n<meta name=\"twitter:card\" content=\"summary_large_image\" \/>\n<meta name=\"twitter:label1\" content=\"Tiempo de lectura\" \/>\n\t<meta name=\"twitter:data1\" content=\"6 minutos\" \/>\n<script type=\"application\/ld+json\" class=\"yoast-schema-graph\">{\"@context\":\"https:\\\/\\\/schema.org\",\"@graph\":[{\"@type\":\"TechArticle\",\"@id\":\"https:\\\/\\\/aobosteel.com\\\/l6-tool-steel-tensile-properties\\\/#article\",\"isPartOf\":{\"@id\":\"https:\\\/\\\/aobosteel.com\\\/l6-tool-steel-tensile-properties\\\/\"},\"author\":{\"name\":\"Evan\",\"@id\":\"https:\\\/\\\/aobosteel.com\\\/#\\\/schema\\\/person\\\/96118415c30ca6bb52eaf1127b052ef7\"},\"headline\":\"L6 Tool Steel Tensile Properties After Tempering\",\"datePublished\":\"2026-10-01T08:08:13+00:00\",\"dateModified\":\"2026-10-15T16:47:15+00:00\",\"mainEntityOfPage\":{\"@id\":\"https:\\\/\\\/aobosteel.com\\\/l6-tool-steel-tensile-properties\\\/\"},\"wordCount\":1132,\"publisher\":{\"@id\":\"https:\\\/\\\/aobosteel.com\\\/#organization\"},\"inLanguage\":\"es\"},{\"@type\":\"WebPage\",\"@id\":\"https:\\\/\\\/aobosteel.com\\\/l6-tool-steel-tensile-properties\\\/\",\"url\":\"https:\\\/\\\/aobosteel.com\\\/l6-tool-steel-tensile-properties\\\/\",\"name\":\"L6 Tool Steel Tensile Properties After Tempering\",\"isPartOf\":{\"@id\":\"https:\\\/\\\/aobosteel.com\\\/#website\"},\"datePublished\":\"2026-10-01T08:08:13+00:00\",\"dateModified\":\"2026-10-15T16:47:15+00:00\",\"description\":\"Measured tensile strength, elongation, reduction of area and hardness for L6 tool steel after tempering from 205 to 650 C, with the L2 with and without vanadium comparison.\",\"breadcrumb\":{\"@id\":\"https:\\\/\\\/aobosteel.com\\\/l6-tool-steel-tensile-properties\\\/#breadcrumb\"},\"inLanguage\":\"es\",\"potentialAction\":[{\"@type\":\"ReadAction\",\"target\":[\"https:\\\/\\\/aobosteel.com\\\/l6-tool-steel-tensile-properties\\\/\"]}]},{\"@type\":\"BreadcrumbList\",\"@id\":\"https:\\\/\\\/aobosteel.com\\\/l6-tool-steel-tensile-properties\\\/#breadcrumb\",\"itemListElement\":[{\"@type\":\"ListItem\",\"position\":1,\"name\":\"\u9996\u9875\",\"item\":\"https:\\\/\\\/aobosteel.com\\\/\"},{\"@type\":\"ListItem\",\"position\":2,\"name\":\"L6 Tool Steel Tensile Properties After Tempering\"}]},{\"@type\":\"WebSite\",\"@id\":\"https:\\\/\\\/aobosteel.com\\\/#website\",\"url\":\"https:\\\/\\\/aobosteel.com\\\/\",\"name\":\"AoboSteel\",\"description\":\"\",\"publisher\":{\"@id\":\"https:\\\/\\\/aobosteel.com\\\/#organization\"},\"potentialAction\":[{\"@type\":\"SearchAction\",\"target\":{\"@type\":\"EntryPoint\",\"urlTemplate\":\"https:\\\/\\\/aobosteel.com\\\/?s={search_term_string}\"},\"query-input\":{\"@type\":\"PropertyValueSpecification\",\"valueRequired\":true,\"valueName\":\"search_term_string\"}}],\"inLanguage\":\"es\"},{\"@type\":\"Organization\",\"@id\":\"https:\\\/\\\/aobosteel.com\\\/#organization\",\"name\":\"AoboSteel\",\"url\":\"https:\\\/\\\/aobosteel.com\\\/\",\"logo\":{\"@type\":\"ImageObject\",\"inLanguage\":\"es\",\"@id\":\"https:\\\/\\\/aobosteel.com\\\/#\\\/schema\\\/logo\\\/image\\\/\",\"url\":\"https:\\\/\\\/aobosteel.com\\\/wp-content\\\/uploads\\\/2025\\\/01\\\/cropped-aobo-steel-1.avif\",\"contentUrl\":\"https:\\\/\\\/aobosteel.com\\\/wp-content\\\/uploads\\\/2025\\\/01\\\/cropped-aobo-steel-1.avif\",\"width\":1052,\"height\":592,\"caption\":\"AoboSteel\"},\"image\":{\"@id\":\"https:\\\/\\\/aobosteel.com\\\/#\\\/schema\\\/logo\\\/image\\\/\"},\"sameAs\":[\"https:\\\/\\\/www.facebook.com\\\/profile.php?id=61565368220197\",\"https:\\\/\\\/www.linkedin.com\\\/in\\\/aobosteel-evan\\\/\"]},{\"@type\":\"Person\",\"@id\":\"https:\\\/\\\/aobosteel.com\\\/#\\\/schema\\\/person\\\/96118415c30ca6bb52eaf1127b052ef7\",\"name\":\"Evan\",\"image\":{\"@type\":\"ImageObject\",\"inLanguage\":\"es\",\"@id\":\"https:\\\/\\\/secure.gravatar.com\\\/avatar\\\/8e402f2e6f36093f0bf1855dbf79269cde23cd659c44eefdd7ecf7ff9c05786f?s=96&d=mm&r=g\",\"url\":\"https:\\\/\\\/secure.gravatar.com\\\/avatar\\\/8e402f2e6f36093f0bf1855dbf79269cde23cd659c44eefdd7ecf7ff9c05786f?s=96&d=mm&r=g\",\"contentUrl\":\"https:\\\/\\\/secure.gravatar.com\\\/avatar\\\/8e402f2e6f36093f0bf1855dbf79269cde23cd659c44eefdd7ecf7ff9c05786f?s=96&d=mm&r=g\",\"caption\":\"Evan\"},\"sameAs\":[\"http:\\\/\\\/www.aobosteel.com\",\"https:\\\/\\\/www.facebook.com\\\/profile.php?id=61565368220197\",\"https:\\\/\\\/www.instagram.com\\\/aobosteel\\\/\",\"https:\\\/\\\/www.linkedin.com\\\/in\\\/aobosteel-evan\\\/\",\"https:\\\/\\\/x.com\\\/AobosteelEvan\",\"https:\\\/\\\/www.youtube.com\\\/@aobosteel\"],\"url\":\"https:\\\/\\\/aobosteel.com\\\/es\\\/blog\\\/author\\\/admin\\\/\"}]}<\/script>\n<!-- \/ Yoast SEO Premium plugin. -->","yoast_head_json":{"title":"Propiedades de tracci\u00f3n del acero para herramientas L6 despu\u00e9s del revenido","description":"Resistencia a la tracci\u00f3n, alargamiento, reducci\u00f3n de \u00e1rea y dureza medidas para el acero para herramientas L6 tras revenido de 205 a 650 C, con la comparaci\u00f3n del L2 con y sin vanadio.","robots":{"index":"index","follow":"follow","max-snippet":"max-snippet:-1","max-image-preview":"max-image-preview:large","max-video-preview":"max-video-preview:-1"},"canonical":"https:\/\/aobosteel.com\/es\/l6-tool-steel-tensile-properties\/","og_locale":"es_ES","og_type":"article","og_title":"L6 Tool Steel Tensile Properties After Tempering","og_description":"Measured tensile strength, elongation, reduction of area and hardness for L6 tool steel after tempering from 205 to 650 C, with the L2 with and without vanadium comparison.","og_url":"https:\/\/aobosteel.com\/es\/l6-tool-steel-tensile-properties\/","og_site_name":"AoboSteel","article_publisher":"https:\/\/www.facebook.com\/profile.php?id=61565368220197","article_modified_time":"2026-10-15T16:47:15+00:00","twitter_card":"summary_large_image","twitter_misc":{"Tiempo de lectura":"6 minutos"},"schema":{"@context":"https:\/\/schema.org","@graph":[{"@type":"TechArticle","@id":"https:\/\/aobosteel.com\/l6-tool-steel-tensile-properties\/#article","isPartOf":{"@id":"https:\/\/aobosteel.com\/l6-tool-steel-tensile-properties\/"},"author":{"name":"Evan","@id":"https:\/\/aobosteel.com\/#\/schema\/person\/96118415c30ca6bb52eaf1127b052ef7"},"headline":"L6 Tool Steel Tensile Properties After Tempering","datePublished":"2026-10-01T08:08:13+00:00","dateModified":"2026-10-15T16:47:15+00:00","mainEntityOfPage":{"@id":"https:\/\/aobosteel.com\/l6-tool-steel-tensile-properties\/"},"wordCount":1132,"publisher":{"@id":"https:\/\/aobosteel.com\/#organization"},"inLanguage":"es"},{"@type":"WebPage","@id":"https:\/\/aobosteel.com\/l6-tool-steel-tensile-properties\/","url":"https:\/\/aobosteel.com\/l6-tool-steel-tensile-properties\/","name":"Propiedades de tracci\u00f3n del acero para herramientas L6 despu\u00e9s del revenido","isPartOf":{"@id":"https:\/\/aobosteel.com\/#website"},"datePublished":"2026-10-01T08:08:13+00:00","dateModified":"2026-10-15T16:47:15+00:00","description":"Resistencia a la tracci\u00f3n, alargamiento, reducci\u00f3n de \u00e1rea y dureza medidas para el acero para herramientas L6 tras revenido de 205 a 650 C, con la comparaci\u00f3n del L2 con y sin vanadio.","breadcrumb":{"@id":"https:\/\/aobosteel.com\/l6-tool-steel-tensile-properties\/#breadcrumb"},"inLanguage":"es","potentialAction":[{"@type":"ReadAction","target":["https:\/\/aobosteel.com\/l6-tool-steel-tensile-properties\/"]}]},{"@type":"BreadcrumbList","@id":"https:\/\/aobosteel.com\/l6-tool-steel-tensile-properties\/#breadcrumb","itemListElement":[{"@type":"ListItem","position":1,"name":"\u9996\u9875","item":"https:\/\/aobosteel.com\/"},{"@type":"ListItem","position":2,"name":"L6 Tool Steel Tensile Properties After Tempering"}]},{"@type":"WebSite","@id":"https:\/\/aobosteel.com\/#website","url":"https:\/\/aobosteel.com\/","name":"AoboSteel","description":"","publisher":{"@id":"https:\/\/aobosteel.com\/#organization"},"potentialAction":[{"@type":"SearchAction","target":{"@type":"EntryPoint","urlTemplate":"https:\/\/aobosteel.com\/?s={search_term_string}"},"query-input":{"@type":"PropertyValueSpecification","valueRequired":true,"valueName":"search_term_string"}}],"inLanguage":"es"},{"@type":"Organization","@id":"https:\/\/aobosteel.com\/#organization","name":"AoboSteel","url":"https:\/\/aobosteel.com\/","logo":{"@type":"ImageObject","inLanguage":"es","@id":"https:\/\/aobosteel.com\/#\/schema\/logo\/image\/","url":"https:\/\/aobosteel.com\/wp-content\/uploads\/2025\/01\/cropped-aobo-steel-1.avif","contentUrl":"https:\/\/aobosteel.com\/wp-content\/uploads\/2025\/01\/cropped-aobo-steel-1.avif","width":1052,"height":592,"caption":"AoboSteel"},"image":{"@id":"https:\/\/aobosteel.com\/#\/schema\/logo\/image\/"},"sameAs":["https:\/\/www.facebook.com\/profile.php?id=61565368220197","https:\/\/www.linkedin.com\/in\/aobosteel-evan\/"]},{"@type":"Person","@id":"https:\/\/aobosteel.com\/#\/schema\/person\/96118415c30ca6bb52eaf1127b052ef7","name":"Evan","image":{"@type":"ImageObject","inLanguage":"es","@id":"https:\/\/secure.gravatar.com\/avatar\/8e402f2e6f36093f0bf1855dbf79269cde23cd659c44eefdd7ecf7ff9c05786f?s=96&d=mm&r=g","url":"https:\/\/secure.gravatar.com\/avatar\/8e402f2e6f36093f0bf1855dbf79269cde23cd659c44eefdd7ecf7ff9c05786f?s=96&d=mm&r=g","contentUrl":"https:\/\/secure.gravatar.com\/avatar\/8e402f2e6f36093f0bf1855dbf79269cde23cd659c44eefdd7ecf7ff9c05786f?s=96&d=mm&r=g","caption":"Evan"},"sameAs":["http:\/\/www.aobosteel.com","https:\/\/www.facebook.com\/profile.php?id=61565368220197","https:\/\/www.instagram.com\/aobosteel\/","https:\/\/www.linkedin.com\/in\/aobosteel-evan\/","https:\/\/x.com\/AobosteelEvan","https:\/\/www.youtube.com\/@aobosteel"],"url":"https:\/\/aobosteel.com\/es\/blog\/author\/admin\/"}]}},"uagb_featured_image_src":{"full":false,"thumbnail":false,"medium":false,"medium_large":false,"large":false,"1536x1536":false,"2048x2048":false,"trp-custom-language-flag":false},"uagb_author_info":{"display_name":"Evan","author_link":"https:\/\/aobosteel.com\/es\/blog\/author\/admin\/"},"uagb_comment_info":0,"uagb_excerpt":"L6 Tool Steel Tensile Properties After Tempering L6 is the low-alloy tool steel that shops reach for when a die has to absorb shock rather than resist abrasion, and the numbers that describe that behaviour are tensile strength, elongation and reduction of area measured on tempered specimens. The tables below collect one L6 heat carried…","rttpg_featured_image_url":null,"rttpg_author":{"display_name":"Evan","author_link":"https:\/\/aobosteel.com\/es\/blog\/author\/admin\/"},"rttpg_comment":0,"rttpg_category":null,"rttpg_excerpt":"L6 Tool Steel Tensile Properties After Tempering L6 is the low-alloy tool steel that shops reach for when a die has to absorb shock rather than resist abrasion, and the numbers that describe that behaviour are tensile strength, elongation and reduction of area measured on tempered specimens. The tables below collect one L6 heat carried…","_links":{"self":[{"href":"https:\/\/aobosteel.com\/es\/wp-json\/wp\/v2\/pages\/20493","targetHints":{"allow":["GET"]}}],"collection":[{"href":"https:\/\/aobosteel.com\/es\/wp-json\/wp\/v2\/pages"}],"about":[{"href":"https:\/\/aobosteel.com\/es\/wp-json\/wp\/v2\/types\/page"}],"author":[{"embeddable":true,"href":"https:\/\/aobosteel.com\/es\/wp-json\/wp\/v2\/users\/1"}],"replies":[{"embeddable":true,"href":"https:\/\/aobosteel.com\/es\/wp-json\/wp\/v2\/comments?post=20493"}],"version-history":[{"count":3,"href":"https:\/\/aobosteel.com\/es\/wp-json\/wp\/v2\/pages\/20493\/revisions"}],"predecessor-version":[{"id":22556,"href":"https:\/\/aobosteel.com\/es\/wp-json\/wp\/v2\/pages\/20493\/revisions\/22556"}],"wp:attachment":[{"href":"https:\/\/aobosteel.com\/es\/wp-json\/wp\/v2\/media?parent=20493"}],"curies":[{"name":"wp","href":"https:\/\/api.w.org\/{rel}","templated":true}]}}